<p>[QUOTE=&quot;Ce BCA, post: 4060215, member: 18716&quot;]I suspect this would be very late 18th or early 19th century.&nbsp; The damage appears to be due to the failed attempt to make a hanging hole during production.&nbsp; Stress at that point has caused the crack to appear over time.&nbsp; The fact that it is 14&quot; is good, far less common than 12&quot; or less.&nbsp; The way the crack is formed is bad news as it may propagate further especially if it is exposed to regular heating and cooling (ie in full sun in a window).&nbsp; Rim chips and glaze losses and minor hairlines are usually acceptable but reduce value, this crack would make it a very hard sell.&nbsp; Unless you want it as a study piece I would pass on it.[/QUOTE]</p><p><br /></p>